Atlas

6 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Austenite Capture method: Transverse Section Aspect clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
SCC of Austenitic SS Flange Stub End
1
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Transverse Section AspectDf - Cracks
Transverse section macrography of the plate where the degradation by thinning is worst, close to the original corners of the tube. The thinning is occurrring from the product reaction side (side A to the bottom of the figure). The macrography shows a reduction in the thickness from 2 mm (right side, sample 2) to almost zero (left side, sample 1).
86
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Transverse Section AspectDf - Thinning
After a longitudinal cut of the case it was possible to see that a localized corrosion has occurred associated to the regions where there were sealed holes, plugged, in a crevice condition, not related to any welded position.
193
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Transverse Section AspectDf - Corrosion
The macrography of a transverse section of the new tube shows that there are shrinkage voids close to the internal surface, that is exposed to high temperature air. The tube is a 4" diameter and 1/4" thick.
62
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure
The macrography of a transverse section of the shell to flange weld (Lepto's etch) shows that the cracking occurred through the shell plate thickness, at the margin of the fillet weld.
93
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Transverse Section AspectDf - Cracking
Transverse section of the 2" diameter pipe at the pitting location. The pipe was leaking.
1323
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Transverse Section AspectDf - Pitting

More from these cases

ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Detail of the case thickness (20 mm) with the through wall localized corrosion in a crevice condition where there was a plug.
98
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Transverse Section AspectDf - Localized Corrosion
ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
The macrography of a transverse section of the tube removed from service after 6 months, with damage close to the internal tube surface. The tube is a 4" diameter and 1/4" thick.
41
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure