“corrosion”

8 cases · 11 images for “corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Capture method: Surface Aspect clear all

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Detail of the internal piping surface, showing lack of deposits and a shinning surface, suggesting erosive conditions.
226
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Surface AspectDf - Leakage
Aspect of the washout in the 5" drill pipe, in the pipe body, after cleaning the surface. The surface presents several parallel tool marks that are not typical in the pipe since the torque is applied in the tool joint.
195
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Surface AspectDf - At the Surface
Internal surface detail of the 3 1/2" pipe, cut in a longitudinal section (transverse to the weld), presenting a localized corrosion at the margin of the welded joint (Keller etched), in the root. The pipeline was assembled with pipes manufactured in two different aluminum alloys, AA 3003 (top of the figure) and AA 6063 (bottom of the figure), and the localized corrosion occurred at the fusion line of the 6063 pipe.
1296
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Surface AspectDf - Welded Joint
Detail of the rusted surface of the knife, before cleaning.
340
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Surface AspectDf - Corrosion
Aspect of the external tube surface after cleaning. It is possible to see that the cracks are longitudinal to the tube and localized in positions where the surface is corroded.
132
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - External Surface
The threads of the carbon steel valve body is corroded. The offshore ambient is wet and chloride rich, creating an aggressive environment for the carbon steel threads.
99
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
Detailed aspect, by a low magnification microscope, of the internal side of the tube, after longitudinal cut. The tube, that is 1.6mm thick, presented several points of localized corrosion leading to leaks.
46
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - Surface AspectDf - Localized Corrosion
Aspect of the tubesheet after removal of the cooper alloy tubes and water cleaning. The corrosion is more intense in the regions of tube connection.
176
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - Surface AspectDf - Corrosion

More from these cases

ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Aspect of the internal tube surface after a longitudinal cut, without cleaning. It is possible to see a clean surface inside the tube.
104
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Internal Surface
Macro view of a bent tube section showing a transverse surface crack with dark staining along the crack path on the outer bend.
0
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - General View
ML00184 — Dissimilar Steels in a Threaded ConnectionM - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Not only the threads were corroded but all regions under the painting that was detached from the surface.
86
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion