“corrosion”

4 cases · 18 images for “corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: AISI Capture method: Scanning Electron Microscope clear all

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Fracture surface aspect at the scanning electron microscopy (SEM) of the clamp OD, showing different planes of propagation of the fracture.
42
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Fractography by SEMDf - Fracture
Tempered martensitic microstructure of the knife observed in a transverse section micrography. There are also secondary carbides (white globules) that increase the material wear resistance.
254
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Kalling Etched Micrography by SEMDf - Martensite
Low magnification SEM image showing the brittle aspect of the cracks in the bolt thread.
61
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Brittle Cracks
Aspect of the spring surface, with a layer of corroded products, and pits.
36
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Surface Aspect by SEMDf - Corrosion

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Detail by scanning electron microscop of the clamp surface showing several cracks, parallel. In this image the cracks appear horizontal, but the photo was taken with the axis of the clamp in the vertical direction which means that the cracks are transverse to the axis.
41
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks
Detailed aspect of the previous figure showing the parallel cracks, transverse to the axis.
37
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Surface Aspect by SEMDf - Multiple cracks
Detail by scanning electron microscopy of the pits in the metallographic longitudinal section of the clamp, at the surface (left side of the image). There are cracks emanating from the pits.
27
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Crack
Detail by scanning electron microscopy of the cracks emanating from the pits in the metallographic longitudinal section of the clamp, at the surface (left side of the image).
25
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Micrography by SEMDf - Crack
Metallographic aspect by scanning electron microscopy of one secondary cracking, paralell to the fracture surface, growthing with an irregular path and transgranular morphologyy.
28
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Micrography by SEMDf - Corrosion Cracking

+3 more from this case →

ML00054 — Cutlery CorrosionM - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Detail of the tempered martensitic microstructure with secondary carbides of the knife, observed in a transverse section micrography.
206
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Kalling Etched Micrography by SEMDf - Martensite
Aspect of the rusted surface after cleaning, showing adhered products at the surface, in regions where the passive layer was destroyed and pitting corrosion occurred.
184
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion
Detail of the rusted surface. EDS analysis inside the pitting shows a high Cl peak (the bright aspect inside the pitting), indicating that the salt over the surface was responsible for destroying the passive layer and the localized corrosion occurred.
172
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Surface Aspect by SEMDf - Corrosion
Micrographic aspect of the pitting corrosion at the knife surface. It is possible to see the typical pitting aspect of a localized corrosion that appears as a small dot at the surface but it is a big crater under the surface.
185
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Micrography by SEMDf - Pitting
Detail of the micrographic aspect of the pitting corrosion at the knife surface.
168
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Micrography by SEMDf - Pitting
ML00157 — Bolts Under Chloride SCC ConditionsM - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Detail of the bolt thread in a SEM image, showing parts of the thread removed in a brittle way.
62
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Brittle Fracture