Microstructure: Small amount of delta ferrite Capture method: Scanning Electron Microscope Detail focus: Weld Metal clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the weld metal presenting columnar grains and martensitic structure.
13
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal

More from these cases

ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Higher magnification of the martensitic structure of the weld metal, in a region where the previous austenitic grains are columnar. Hardness level of 350HV10.
12
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Micrographic detail of the weld metal presenting equiaxial grains grains and martensitic structure. There are also multiples globular inclusions, caracteristic of a welding process that uses flux.
10
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Higher magnification of the martensitic structure of the weld metal, hardness level of 350HV10.
10
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Micrographic detail of a non metallic inclusion in the weld metal of a joint between the original casting blade remanufacture by welding and an insert casting. The EDS analysis indicated the presence of the elements Ti, Zr, Si and O in the inclusion.
37
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by SEMDf - Weld Metal