2 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Blade Condition: Damage Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification image by scanning electron microscopy. In the bottom of the image the fracture appearance is brittle and presenting several secondary cracks. In the top of the image the fracture is fully flat, also without macroscopic plastic deformation.
33
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fractography by SEMDf - Fracture
Micrography of the blade, view inside the grain. The intragranular precipitation presents one unique size of precipitation, not yet coalesced, although the blade was in high temperature service for 50.000 hours. Etched by H2SO4 + HNO3 + H3PO4 reagent.
66
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Intragranular Secondary Precipitation

More from these cases

ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
The position of the fracture at the starting point of the failure is brittle, transgranular, with a cleavage/quase-cleavage morphology.
24
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fractography by SEMDf - Cleavage Facets
Aspect by SEM of the secondary crack at the blade surface.
18
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Surface Aspect by SEMDf - At the Surface
At the surface of the blade there are microcracks with a brittle aspect.
23
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Surface Aspect by SEMDf - Secondary Cracks
SEM fractograph showing a cleavage facet with radiating river-pattern markings and scattered fine surface particles.
1
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fractography by SEMDf - Cleavage Facets
ML00042 — Gas Turbine Blade IN 939, CoatedM - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Micrographic detail of the diffusion coating. H2SO4 + HNO3 + H3PO4 etched.
47
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Coating