Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Tube Microstructure: Austenite Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in the colder part of the equipment, position 1. The material presented carbide precipitation at grain boundaries (not yet fully surrounding the grains) and at this point the tube presented no internal corrosion.
338
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of a longitudinal section of the pipe showing that the carbon steel pipe is slightly banded and there is a decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
125
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

More from these cases

ML00086 — Intergranular Corrosion of Sensitized 304SSM - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 2, where the temperature was higher and the carbide precipitation increased during service.
272
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 3, where intergranular and transgranular carbide precipitation occurred during service.
234
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intragranular Secondary Precipitation
Micrography of a longitudinal section of the tube in position 2, presenting thinning by intergranular corrosion at the internal surface.
193
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion
Micrographic detail of the intergranular corrosion at the internal surface of the tube in position 2. Several grains were already removed by the corrosion.
171
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion
Micrography of a longitudinal section of the tube in position 3, at the internal surface. Although there is a strong precipitation, both intergranular and transgranular, the tube did not corrode at this point.
144
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intragranular Secondary Precipitation

+1 more from this case →

ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Micrography of a longitudinal section of the pipe showing the carbon steel pipe , internal.
122
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of a longitudinal section of the pipe showing the stainless steel pipe , external.
99
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrographic detail of the interface in the longitudinal section of the pipe showing the Vickers (300g) microhardness values, close to the interface in the carbon steel side and in the stainless steel side. Although the Nital etch does not allow to reveal the structure in the stainless steel side, the high hardness values show that the structure is different.
113
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of the interface in the longitudinal section of the pipe showing the decarburized layer at the solid solution welded interface. The stainless steel structure (in the right side of the figure) is not revealed using the Nital etch.
80
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Clad Interface
Micrography of the interface between the carbon steel that is strongly etched by the electrolytic oxalic acid (in the left side of the figure) and the stainless steel, in the longitudinal section of the pipe. There is a strain hardened layer very close to the interface, at the stainless steel side.
79
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Longitudinal Section