Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Alpha Capture method: Optical Microscope Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the secondary crack from the fracture surface of the WHEEL 1, following the interdendritic precipitates.
36
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Keller Etched Micrography by OMDf - Fracture
Micrographic aspect of the weld metal presenting brittle detached parts in the starting point of the fracture, in the weld metal, and several fatigue cracks propagating from the stress concentration raisers.
23
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Fatigue Crack
In a cut perpendicular to the macroscopic secondary crack it is possible to see several brittle microcracks (branched), indicating that an embrittlement has occurred.
22
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - As polished micrographyDf - Brittle Cracks
Micrography of a transverse section of the tube, close to the leakage point. The thickness is localized reduced where the internal passive layer was ruptured, and the chemical effect of the biological proliferation created a high corrosion rate.
26
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Localized Thinning
Micrography of a transverse section of the bent tube, external surface (OD) to the top and internal surface (ID) to the bottom of the figure. At the through wall cracking position, the external surface presented a layer of intergranular corrosion.
95
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Cracking
The pipe base metal, at the internal surface, presents a hydride layer showing that the environment is absorbing hydrogen. Although there are microcracks in this layer it did not detach in the base metal.
102
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Hydride Formation

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Dendritic branching structure of the aluminum matrix, with fine interdendritic features visible against a darker surrounding phase.
2
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Keller Etched Micrography by OMDf - Crack
ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Micrographic detail of transgranular propagation of the cracking by fatigue.
34
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Fatigue Crack
Hydrides in Titanium Weld
1
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Micrography by OMDf - Hydride Formation
ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
The main crack is to the top and the blade surface is to the right, in this micrography that does not reveal any plastic deformation, with transgranular and integranular cracks.
24
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Brittle Fracture
Transgranular and integranular cracks in the alpha matrix full of acicular hydrides .
17
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Hydride Formation
ML00170 — MIC in Aluminum Brass TubesM - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
MIC in Aluminum Brass Tubes
2
VIEW
ML00170 / Sep.2020
MIC in Aluminum Brass Tubes
M - Aluminum BrassP - Seamless tubeAp - MaritimeCd - Preferential Dissolution
Cm - FeCl3+HCl+Ethanol Etched MicroDf - Localized Corrosion
ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Micrographic detail of the external side of the bent tube, as polished, showing detachement of several grains due to the intergranular corrosion layer. The corroded layer is about 200 microns thick at this position.
89
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Intergranular Corrosion
Micrographic detail of the external side of the tube, showing the layer of intergranular corrosion and the through ewall integranular stress corrosion cracking.
88
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Through Wall Cracking
Micrography close to the external surface (to the top). The layer of intergranular corrosion shows evidences of selective leaching (suggesting that the aluminum was preferentially consumed). The stress corrosion cracking starts from the intergranularly corroded layer.
113
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Intergranular Cracking
Micrographic detail of the intergranular corroded layer with evidences of selective leaching.
43
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Intergranular Corrosion
Micrographic detail of the intergranular stress corrosion crack, without evidences of dealloying.
48
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Stress Corrosion Cracks
ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
The pipe internal suface, at the welded region, presents no hydride layer (because it has detached) as well as the material itself is suffering brittle detachment.
71
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Localized Thinning
Detail, as polished, of brittle cracks in the weld metal, from the internal side of the pipe.
67
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by OMDf - Brittle Cracks
Seam weld of the pipe showing the localized thinning in the weld metal, caused by the detachment of the hydride layer and brittle behaviour of the coarse weld metal structure.
64
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Kroll Etched Micrography by OMDf - Localized Thinning