Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 898-1 Capture method: Optical Microscope Detail focus: Crack clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section, at the fillet that was tightened (to the end of the bolt) adjacent to the fracture. The cracking is typical of localized overloading, probably because it was only partially tightened in the tapped hole.
104
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Crack

More from these cases

ML00130 — Fatigue Fracture of Overloaded BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Micrographic detail of the cracking adjacent to the fracture. It is a secondary cracking that was created by overloading and was propagating by fatigue.
90
VIEW
ML00130 / Jun.2018
Fatigue Fracture of Overloaded Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - O&G Well DrillingCd - Mechanical Fatigue
Cm - Nital Etched Micrography by OMDf - Crack