3 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Dendritic Capture method: Optical Microscope Detail focus: Base Metal clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the pipe substrate, in low magnification, showing a uniform microstructure,
79
VIEW
ML00132 / May.2018
Seamless Pipe Overlaid with Alloy 625
M - LAS / Ni AlloyP - Seamless PipeAp - Oil and GasCd - Welding
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of the cast rim, base metal, in the as polished condition, showing the dendrites of alpha aluminum and interdendritic eutectic Si/alpha, silicon particles in a coalesced condition that sugegsts a solution annealed treatment.
119
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by OMDf - Base Metal
Micrography of the pipe longitudinal base metal.
148
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side

More from these cases

ML00070 — Automotive Light Alloy Wheel Repaired By WeldingM - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Micrography of the cast rim, base metal, showing the dendrites of alpha aluminum and interdendritic eutectic Si/alpha, silicon particles in a coalesced condition that suggests a solution annealed treatment. After etching it is possible to identify a transgranular precipitation (aging) and a dark FeSiAl phase (neddles).
87
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Base Metal
Micrographic detail of the cast rim, base metal, in the as polished condition, showing the dendrites of alpha aluminum and interdendritic eutectic Si/alpha, silicon particles in a coalesced condition that sugegsts a solution annealed treatment.
74
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Micrography by OMDf - Base Metal
Micrographic detail of the cast rim, base metal, showing the dendrites of alpha aluminum and interdendritic eutectic Si/alpha, silicon particles in a coalesced condition that suggests a solution annealed treatment. After etching it is possible to identify a transgranular precipitation (aging) and a dark FeSiAl phase (neddles).
62
VIEW
ML00070 / Jan.2019
Automotive Light Alloy Wheel Repaired By Welding
M - Aluminum Silicon MagnesiumP - RimAp - AutomotiveCd - Removed From Service
Cm - Keller Etched Micrography by OMDf - Base Metal
ML00065 — Erosion Corrosion of Monel PipingM - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Micrographic detail of the pipe base metal presenting a granular microstructure. Some inclusions are also visible.
142
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Micrography of the elbow base metal. The comparison with the pipe micrography shows an important difference of thickness.
132
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side
Elbow base metal micrographic detail presenting a granular microstructure. Like the pipe, the microstructure reveals inclusions.
106
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side