Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Corrosion Microstructure: Granular Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
76
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Micrography of the pipe longitudinal base metal.
148
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Micrography of a longitudinal section of the pipe AA 3003. Granular structure that reveals the forming direction and dispersed particles.
229
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Base Metal Left Side
Transverse section of the fitting that suffered a longitudinal cracking. As polished. The wrought fitting has suffered intergranular stress corrosion cracking from the internal surface, exposed to hot caustic environment.
566
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Micrography by OMDf - Intergranular Cracking

More from these cases

ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Optical micrography of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
64
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transverse Section
Micrographic detail of the transverse section of the drill collar, in the center of the thickness, presenting an uniform, granular, fully austenitic microstructure.
61
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked. The material presented 38HRc hardness.
58
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Optical micrography of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
62
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Longitudinal Section
Micrographic detail of the longitudinal section of the drill collar, in the center of the thickness, presenting slightly elongated grains of fully austenitic microstructure, cold worked.
59
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite

+6 more from this case →

ML00065 — Erosion Corrosion of Monel PipingM - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Micrographic detail of the pipe base metal presenting a granular microstructure. Some inclusions are also visible.
142
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Micrography of the elbow base metal. The comparison with the pipe micrography shows an important difference of thickness.
132
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side
Elbow base metal micrographic detail presenting a granular microstructure. Like the pipe, the microstructure reveals inclusions.
106
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side
Micrography of the pipe heat affected zone. The weld metal is on the right.
91
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Fusion Line Left Side
Micrographic detail of the pipe fusion line. The pipe heat affected zone is at the bottom and the weld metal is at the top.
86
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched Micrography by OMDf - Fusion Line Left Side

+11 more from this case →

ML00059 — Intergranular Corrosion of Aluminum PipingM - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Micrographic detail of a longitudinal section of the pipe AA 3003. Granular structure and dispersed particles.
199
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Base Metal Left Side
Micrography of a longitudinal section of the pipe AA 6063. Granular structure and dispersed particles.
169
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Base Metal Right Side
Micrography of the Fusion Line of the AA 3003 pipe, presenting a narrow HAZ.
127
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Fusion Line Left Side
Micrography of the Fusion Line of the AA 3003 pipe, presenting a narrow HAZ.
110
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Fusion Line Left Side
Micrographic detail of the Fusion Line of the AA 3003 pipe, presenting a narrow HAZ.
93
VIEW
ML00059 / Feb.2018
Intergranular Corrosion of Aluminum Piping
M - Aluminum ManganeseP - Welded JointAp - Chemical IndustryCd - Intergranular Corrosion
Cm - Keller Etched Micrography by OMDf - Fusion Line Left Side

+9 more from this case →

ML00011 — Intergranular SCC of Pure NickelM - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
113
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
110
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
96
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
Transverse section of the fitting that suffered a longitudinal cracking. As polished. The wrought fitting has suffered intergranular stress corrosion cracking from the internal surface, exposed to hot caustic environment.
70
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Micrography by OMDf - Intergranular Cracking
Transverse section of the fitting that suffered a longitudinal cracking. As polished. The wrought fitting has suffered intergranular stress corrosion cracking from the internal surface, exposed to hot caustic environment.
59
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Micrography by OMDf - Corrosion Cracking

+2 more from this case →