Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Corrosion Capture method: Optical Microscope Detail focus: Cracks clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a typical corrosion-fatigue mechanism, in a longitudinal section. The loss of material is accelerated a lot by the cracks through the thickness.
42
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Cracks
Micrographic aspect of the Cr layer at the surface presenting incipient damage. Microcracks of the Cr layer, associated to small pits.
62
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Micrography by OMDf - Cracks
Micrographic detail of the dezincification effect, where the beta phase is preferentially corroded, leaving a cooper rich phase (red) that is porous and easily cracks.
130
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Cracks