Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Corrosion Fatigue Capture method: Nital Etched Micrography by SEM clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Detail by scanning electron microscopy of the pits in the metallographic longitudinal section of the clamp, at the surface (left side of the image). There are cracks emanating from the pits.
27
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Crack
Micrographic detail, by scanning electron micrography, of the pitting corrosion generating cracks, typical of a corrosion fatigue mechanism.
156
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Pitting

More from these cases

ML00171 — Corrosion Fatigue of U Bolt Pipe ClampM - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Metallographic aspect of one secondary cracking, paralell to the fracture surface, growthing with an irregular path and transgranular morphologyy. The main crack presents small branching and cleavage propagation with a clear influence of corrosion (hydrogen evoution) .
27
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Corrosion Cracking
ML00163 — Corrosion Fatigue of a Boiler Waterwall TubeM - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Micrographic detail, by scanning electron microscopy, of the external tube surface, presenting the crack at the weld margin. The microstructure if ferritic in the left side (weld metal) and bainitic in the right side of the crack (heat affected zone).
90
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Cracking
Corrosion Fatigue of a Boiler Waterwall Tube
4
VIEW
ML00163 / Jun.2020
Corrosion Fatigue of a Boiler Waterwall Tube
M - Low Carbon SteelP - Seamless tubeAp - BoilerCd - Corrosion Fatigue
Cm - Nital Etched Micrography by SEMDf - Pearlite