Atlas

9 cases · 14 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint Capture method: NItal Etched Macro clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a section longitudinal to the pipe and transverse to the weld. The thickness of the pipe is 12,7 mm (1/2") and it was welded in 6 passes, the root pass, one fill pass and four cap passes.
855
VIEW
ML00153 / Jan.2019
X52 in a Tubular Structure
M - CMn SteelP - Seamless PipeAp - StructureCd - Qualified
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the welded joint taken from the vertical up part of the joint, presenting the root in one pass, the fill of the joint in three passes, the cap in three passes and two temper bead passes. The 10" diameter tube, 9.5mm thick, was welded by GTAW in the root (80SD2 filler metal) and by SMAW for fill, cap and temper bead passes (10018-D2 filler metal).
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the plate (thickness 22mm, in horizontal position) to tube (thickness 12.5 mm, in vertical position) welded joint. The half V groove was welded from the top (position inside the combustion chamber) in five weld beads, and with a small fillet welded from the water side (ouside of the tube). Average hardness of the plate is 180HV1 (1kg), of the tube is 150HV1 and of the weld is 190HV1. Maximum hardness of the tube HAZ is 165HV1 and plate HAZ is 195HV1.
219
VIEW
ML00119 / Feb.2018
Thermal Fatigue of a Marine Boiler
M - Low Carbon SteelP - Fabrication WeldAp - ShipCd - Thermal Fatigue
Cm - NItal Etched MacroDf - Welded Joint
Transversal section of the 625 nickel alloy multipass weld. Pipe of 1 1/4' thickness
72
VIEW
ML00066 / May.2017
GMAW Welded Joint in 9%Ni Alloy Steel
M - Nickel Alloy SteelP - Welded Testpiece for QualificationAp - PipelineCd - Welding
Cm - NItal Etched MacroDf - Welded Joint
The macrography of a longitudinal section of the pipe and connector, at the welded joint, shows that the welding was conducted from both side of the groove, starting from the ID and finishing from the OD, ID later machined flush. The cracking was detected by ultrasonic test and the macro shows that it is at the fusion line, growthing into the weld metal. See the schematic drawing in the next figure
535
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Longitudinal Section
Macrography of the typical welded joint between the superior plate (8mm) and the inferior plate (12 mm) using one SAW fillet. The superior plate is welded in the thickness and the inferior plate is welded at the surface in this overlap joint. See the schematic drawing in the next figure
95
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Macrographic aspect of a transverse section of the sample with multiple cracks that were deep in the weld metal.
71
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - NItal Etched MacroDf - Weld Metal
Macrography of the joint welded by SAW process in overlap geometry, between the 8 mm low carbon steel plate (superior) and the 12 mm C-Mn steel plate (inferior).
70
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint

More from these cases

ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Hot cracking at the fusion line of the connector side, in a welded joint between a forging and a pipe, in a macrographic sample. The region of the heat affected zone of the connector presents a dendritic aspect suggesting that the forging reduction rate of the connector was not too high and did not broke the cast structure.
110
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
ML00069 — Liquation Cracks in SAW of Low Carbon SteelM - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
The macrography presents the position of the fracture in the superior plate (8 mm thickness).
61
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Fracture
The macrography presents the position of the fracture in the fillet weld side.
67
VIEW
ML00069 / May.2017
Liquation Cracks in SAW of Low Carbon Steel
M - Low Carbon SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Fracture
ML00067 — Cold Cracks in C-Mn SAW Weld MetalM - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Macrography of the welded joint in a non cracked region.
57
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
Macrography of the welded joint in a cracked region.
49
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint