Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: NItal Etched Macro Detail focus: Microstructure clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a transverse section of a sound tooth, presenting a carburized layer of about 3 mm depth.
87
VIEW
ML00181 / Apr.2022
Wear of a Carburized Hypoid Gear
M - Low Alloy for Thermochemical TreatmentP - Pinion-crown assemblyAp - ShipCd - Wear
Cm - NItal Etched MacroDf - Carburized Layer
Macrography of a circumferential section of the roller bearing, showing two different structures: one, white and hard (64 HRc), close to the external surface; and the other, dark and soft (21 HRc), close to the internal surface. The hardness in the thickness, close to the interface, is about 50 HRc.
122
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - NItal Etched MacroDf - Duplex structure
Macrography of the longitudinal section of the 2" diameter pin close to the fracture surface (top of the figure) in a section where the pin presented the final fracture (it is deformed). The lubrication hole is in the right side of the figure. It is possible to see several secondary cracks at the surface of the pin (left side of the figure), propagating only where there is a carburized layer. It is possible to see that the end of each secondary crack is blunted.
67
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Carburized Layer
Micrography of the fusion line of the second pass (not reheated). The HAZ is bainitic and the weld metal presents columnar grains (of the previous austenite).
60
VIEW
ML00053 / Mar.2017
SAW Longitudinal Seam of X70 Pipe
M - Microalloyed SteelP - Longitudinal Seam Welded PipeAp - SubseaCd - Welding
Cm - NItal Etched MacroDf - Fusion Line