Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite Capture method: NItal Etched Macro Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrographic detail of the longitudinal section of the valve body, at the cracked position, a little far from the actuator hole. There is a straight crack, transverse to the thickness that clearly propagated by fatigue mechanism, from the region where the welding defects were created.
27
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Fatigue Crack
Macrography of a longitudinal section of the pipe at the fracture position, in the thicker thickness. The external side of the pipe (OD) is to the rigth side of the figure, and the internal side of the pipe is to the left of the figure. There are several secondary cracks, opened to the OD, created during bending.
37
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Plastic Deformation
Macrography of a stud longitudinal sectiion at the fracture position (top of the figure). It is possible to see a large secondary crack at the bottom of the thread fillet adjacent to the fracture surface, without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
56
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Secondary Cracks
Macrography of a "longitudinal" section of the padeye showing casting defects close to the internal diamater and a secondary crack, paralel to fracture, starting from the internal diameter. The fracture is not presented in this macro, it is to the top of the photo.
17
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - NItal Etched MacroDf - Cracking
Macrography of the longitudinal section of the pipe presenting multiple cracks from the tool marks.
122
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - NItal Etched MacroDf - Cracks Transverse to the Surface

More from these cases

ML00162 — Valve Body Crack Growth from Weld DefectsM - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Valve Body Crack Growth from Weld Defects
2
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Crack
Valve Body Crack Growth from Weld Defects
1
VIEW
ML00162 / Apr.2020
Valve Body Crack Growth from Weld Defects
M - Low Alloy Medium Carbon QTP - Valve BodyAp - O&G Well DrillingCd - Fatigue Induced by a Defect
Cm - NItal Etched MacroDf - Fatigue Crack
ML00159 — Collapse of a Drill PipeM - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Macrography of a longitudinal section of the pipe at the fracture position, in the thinner thickness. The external side of the pipe (OD) is to the left side of the figure, and the internal side of the pipe is to the rigth of the figure. The fracture occurred by shearing the pipe in a single event (probably due to tensile stresses during removal).
37
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Ductile Fracture
Macrographic detail of the longitudinal section of the pipe at the fracture position, in the thicker thickness. The several secondary cracks, opened to the OD, were created during bending and shows evidences of compression, responsible for the increase in the pipe thickness.
33
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Ductile Fracture
Macrographic detail of a longitudinal section of the pipe at the fracture position, in the thinner thickness. The external side of the pipe (OD) is to the left in the figure, and the internal side of the pipe is to the rigth in the figure. The fracture occurred by shearing the pipe in a single event (probably due to tensile stresses during removal).
24
VIEW
ML00159 / Mar.2020
Collapse of a Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - O&G Well DrillingCd - Ductile Behavior
Cm - NItal Etched MacroDf - Ductile Fracture
ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Macrographic detail of the secondary crack, paralel to fracture, starting from the internal diameter of the padeye. The dendritic structure is evident.
13
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - NItal Etched MacroDf - Secondary Cracks