Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Dendritic Capture method: Micrography by OM using A262 Method A clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the case, observed in the center of the thickness, showing an equiaxial granular austenitic microstructure, free from carbides. The structure is typical of a 316 SS, in a solution annealed condition.
176
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Austenite

More from these cases

ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Micrographic detail of the fully austenitic granular structure of the case, in the center of the thickness.
158
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Austenite
Microstructure of the welded region of the padeye, at the fusion line. The weld metal is dendritic, austeno ferritic, in the left side of the figure. The heat affected zone is in the center of the figure and shows no changes in relation to the base metal. The padeye base metal is to the right side of the figure.
120
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Welded Joint
Micrographic detail of the fusion line of the welded joint of the padeye. The connector where the padeye was installed was welded to the case, but presented no evidences of corrosion.
110
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Welded Joint
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition.
85
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion
Micrographic detail of the crevice corrosion in the case wall, showing that the structure is not affected and is fully austenitic with equiaxial grains typical of a solution annealed condition.
72
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Micrography by OM using A262 Method ADf - Localized Corrosion

+2 more from this case →