Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint Capture method: Kalling Etched Macro clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the flat position welded joint. It was welded in three passes, with the following parameters. Root pass - 159A, 21V, 147mm/s (wire speed), 3.5 mm/s (welding speed), 979 J/mm. Second pass - 170A, 22V, 168mm/s (wire speed), 7.7 mm/s (welding speed), 538 J/mm. Third pass - 172A, 23V, 168mm/s (wire speed), 7.0 mm/s (welding speed), 587 J/mm.
43
VIEW
ML00118 / Jan.2018
Non qualified GMAW of Aluminum Plates
M - Aluminum Magnesium ManganeseP - Welded Testpiece for QualificationAp - ShipCd - Non qualified
Cm - Kalling Etched MacroDf - Overhead Position
Macrography of a longitudinal section of the fitting to tubing weld, with the longitudinal cracking at the tubular fitting position.
69
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Kalling Etched MacroDf - Longitudinal Section
Macrography of the welded joint upper part. Transverse section showing the different zones studied in this ML. See the schematic drawing in the next image.
454
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint
Macrography of a transverse section of the welded joint between the original casting and the inserted casting, in the side of the original part.
23
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched MacroDf - Fusion Line Left Side
The macrography of a transverse section shows the carbon steel tube, externally cladded with stainless steel. The tube was removed from service where it was welded to other tubes to form a wall.
156
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Kalling Etched MacroDf - Transverse Section

More from these cases

ML00094 — MIC of a Subsea Hydraulic LineM - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Macrography of the fitting to tubing welded joint. The internal surface of the fitting (left side) is rough compared to the internal surface of the tubing (right side). The cracking is located only in the fitting and presented no association with the welded joint.
41
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Kalling Etched MacroDf - Longitudinal Section
ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Macrography of the welded joint, at the root position, presenting the different zones studied in this ML. Transverse section. See the schematic drawing in the next image.
47
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Macrography of a transverse section of the welded joint between the original casting and the inserted casting, in the side of the inserted part.
17
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched MacroDf - Fusion Line Right Side