Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Kalling Etched Macro Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrographic detail close to the internal diameter (ID in the bottom), where the cracks were detected by dye check (after removal of the damaged part of the cast fitting). Close to the surface it is possible to see the layers of the weld metal that corresponds to the cast fitting buttering.
21
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched MacroDf - Cracks
17-4 PH rod, tubular, OD 10.6mm, wall thickness about 3.5 mm. Macrography of the rod in a transverse section showing the pitting in a position where it is almost through wall.
86
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched MacroDf - Pitting
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
49
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Intergranular Cracking
Macrography of the pipe to fitting welded joint, in a region very close to the leakage. The sligthly localized thinning is in the weld metal close to the elbow.
53
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Kalling Etched MacroDf - Thinning
Linear indication in the sample, after metallographic preparation. The "cracking" is a casting defect.
65
VIEW
ML00017 / Apr.2017
Casting Defect in CA6NM
M - Martensitic Stainless SteelP - Machined PartAp - EnergyCd - Casting Defect
Cm - Kalling Etched MacroDf - Crack

More from these cases

ML00173 — Welding Cracks in an Aged HP Cast FittingM - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Welding Cracks in an Aged HP Cast Fitting
2
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched MacroDf - Cracks