6 cases · 12 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Hydrogen Capture method: Fracture Surface Aspect clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The through wall cracking was opened by longitudinal cutting of the pipe in two positions, to analyzed the region where the crack was nucleated.
32
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
Macroscopic aspect of the fracture surface.
37
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
Aspect of the bolt fracture, presenting a flat surface.
80
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Macroscopic detail of the fracture surface with a starting point at the external surface of the pin.
82
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Detail of the flat fracture surface of the pin, after disassembling from the TJ box. ID in the top and OD in the bottom of the figure. Radial marks are clear in the fracture surface.
57
VIEW
ML00088 / Dec.2017
Hydrogen Cracking of an API 5D S135 Drill Pipe
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
Fracture view presenting two diferente aspects, brittle in the bottom of the figure and in the center (most part of the fracture) and ductile in the top of the figure. Nominal diameter of the bolt 1 1/2".
203
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - General View

More from these cases

ML00179 — Hydrides in Titanium WeldM - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Aspect of the opened crack, showing the flat fracture. The through wall cracking started at the welded region at the end of the rib.
38
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
Hydrides in Titanium Weld
3
VIEW
ML00179 / Feb.2022
Hydrides in Titanium Weld
M - Unalloyed TitaniumP - In Field WeldAp - Chemical IndustryCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fracture
ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
The propagation of the crack is also transgranular, without plastic deformation, by fatigue.
26
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fracture Surface AspectDf - Fatigue Striation
Aspect of the broken part of the blade that felt and was removed without disassembling the instrument. The fracture is to the top and at the blade surface it is possible to see secondary cracks propagating from the main crack.
22
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Fracture Surface AspectDf - Secondary Cracks
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
The fracture, that occurred at the region of transition between the threaded body and the bolt head, presented a flat and brittle aspect.
69
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Brittle Fracture
ML00074 — Hydrogen Cracking of a 17-4 PH Subsea BoltM - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Detail of the brittle part of the bolt fracture, presenting a secondary cracking longitudinal to the bolt axis. The region of the bolt at the bottom of the thread (close to the surface) is brighter than the internal part of the bolt suggesting different fracture mechanisms.
111
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Fracture Surface AspectDf - Fracture