Atlas

3 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Tubular Forging Capture method: Aspect Before Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the male part of the coupling, a pin, presenting the thermal spray layer detachment (right side of the figure). The pin was manufactured in a superduplex stainless steel tubular forging; the external surface was partially coated by thermal spray and machined. The sealing is only elastomeric but a coating is required to avoid galling between the two materials of the coupling.
1154
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - Aspect Before AnalysisDf - Layer Detachment
Aspect of the internal side of the drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained uncleaned for a period a little longer than 1 month.
775
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Internal Surface
Drilling tool that broke close to the region of the male connector (pin end). The fracture is at the right side of the figure.
102
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture

More from these cases

ML00135 — MIC of a Non Magnetic Drilling ToolM - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Aspect of the external side of the nominal diameter 6 3/4" drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained for a period a little longer than 1 month. This tool is a high strength steel, cold worked.
163
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - General View
Aspect of the external side of the nominal diameter 6 3/4" drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained for a period a little longer than 1 month. This tool is a high strength steel, cold worked.
125
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Localized Corrosion
Detailed aspect of the corroded region in the external side of the drilling tool, after cleaning .
85
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Corrosion
Aspect of the internal side of the drilling tool, after cleaning for inspection. Several regions of corrosion where detected where the drilling mud was adhered and remained for a period a little longer than 1 month. This tool is a high strength steel, cold worked.
48
VIEW
ML00135 / May.2018
MIC of a Non Magnetic Drilling Tool
M - High Mn Austenitic SteelP - Tubular ForgingAp - O&G Well DrillingCd - Pitting Corrosion
Cm - Aspect Before AnalysisDf - Corrosion
ML00082 — Corrosion Fatigue of a Drilling ToolM - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
The fracture was removed from the failed part and analyzed separately. The aspect of the fracture surface is presented. It is flat, with regions of fatigue propagation and with regions of erosion by washout (to the right side of the figure).
80
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fracture
Detail of the fracture surface presenting a fatigue propagation from the outside of the tool.
69
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
Detail of the fracture surface presenting erosion by a washout, because the equipment was pressurized when the cracking became through wall.
63
VIEW
ML00082 / Dec.2017
Corrosion Fatigue of a Drilling Tool
M - Low Alloy Medium Carbon QTP - Tubular ForgingAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Aspect Before AnalysisDf - Washout