Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Intragranular Intergranular Precipitates Capture method: As polished micrography clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
SAMPLE 1 AT 1 mm THICKNESS - Micrography in low magnification in the center of the thickness, as polished. There are no regions of internal damage (like internal voids or cracks), indicating that the mechanism is only related to surface effects.
42
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - In the Center of the Thickness

More from these cases

ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
SAMPLE 3, CLOSE TO THE SURFACE OF SIDE A - Micrography, as polished, of the oxides at the process side. In this region there is an oxide layer, not continuous but with no localized penetrations.
43
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface
SAMPLE 3, CLOSE TO THE SURFACE OF SIDE B - Micrography, as polished, of the oxides at the electric furnace environment side. In this region the oxide layer is thinner than in the process side.
46
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface
SAMPLE 1, CLOSE TO THE SURFACE OF SIDE A - Micrography, as polished, of the oxides at the process side. In this region the oxide layer is penetrating into the austenitic grain boundaries, creating a crack like effect.
56
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface
SAMPLE 1, AT THE FRACTURE - Micrography, as polished, of the oxides at the fracture (zero thickness). In this region the oxide layer penetrated through thickness, intergranular, and fractured the material.
63
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - Intergranular Fracture
SAMPLE 1, AT THE FRACTURE - Micrographic detail, as polished, of the oxides that are penetrating in the austenitic grain boundaries. The oxidation created intergranular cracks in regions close to the edge of the rectangular tube, that are more susceptible to suffer cyclic thermal stresses, since the furnace is weekly turned off, during two days.
55
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - Intergranular Cracking