Atlas

2 cases · 2 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Subsea Capture method: Kalling Etched Macro Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
17-4 PH rod, tubular, OD 10.6mm, wall thickness about 3.5 mm. Macrography of the rod in a transverse section showing the pitting in a position where it is almost through wall.
86
VIEW
ML00121 / Feb.2018
Pitting Corrosion in a Subsea System
M - Austenitic / MartensiticP - Rod & CylinderAp - SubseaCd - Pitting Corrosion
Cm - Kalling Etched MacroDf - Pitting
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks. There is a large amount of delta phase precipitated intergranular and intragranluar.
49
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched MacroDf - Intergranular Cracking