Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Offshore Capture method: Scanning Electron Microscope Detail focus: Weld Metal clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the weld metal tempered martensitic microstructure.
25
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by SEMDf - Weld Metal
Micrographic detail of the ferritic structure in the weld metal close to the low alloy steel tube, by scanning electron microscopy. The weld metal presents a typical aspect for high strenght weld metal (100% acicular ferrite).
32
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Weld Metal

More from these cases

ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Micrographic detail of the ferritic structure in the weld metal close to the carbon steel plate, by scanning electron microscopy. The weld metal presents a typical aspect for low strenght weld metal (grain boundary and primary ferrite, plus acicular ferrite).
30
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Weld Metal
Micrographic detail of the weld metal presenting 100% of acicular ferrite. Although the adopted filler metal was of a low strenght type, the dilution of the tube chemistry in the weld created a typically high strenght weld metal.
26
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Weld Metal
Micrographic detail in higher magnification of the weld metal presenting 100% of acicular ferrite. It is interesting to observe that the previous austenite grain boundary can be seen but there is no primary ferrite in the grain boundary.
36
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Weld Metal