UNS

3 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Finished Product Capture method: Testpiece aspect clear all

UNS — sub-branches

A03560 2A08500 1C12000 1C85710 1C92200 1C95300 1F32800 1F34800 1G10200 2G10450 2G10550 1G10700 2G10800 2G10900 1G12110 1G15220 mod 1G41300 3G41400 3G43400 1G48200 1G61500 1G86300 1J91540 1K03101 2N04400 1N07718 6N08705 1R50400 1S15500 1S17400 3S17700 1S21800 2S30400 1S31600 3S31603 1S32304 1S32750 4S32760 1S40900 1S42000 2S43100 mod 1T31501 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification view of the broken tensile specimen fracture surface. The same macroscopic aspect as the WHEEL 1 fracture surface.
48
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Ductile Fracture
Aspect of the broken tensile testpiece, cylindrical, in a longitudinal direction in the tubular casting, showing zero elongation and zero area reduction. The Yield Strenght (348MPa) is very close to the Ultimate Strenght (352MPa) in the tensile test. Yield to Ultimate ratio of 0.98.
29
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Testpiece aspectDf - Broken Testpiece
The spring fracture was rusted and did not allow the fractographic analysis. The quasecleavage and intergranular fracture micromechanisms presented in this scanning electron microscopy image were obtained from the Charpy V broken testpiece that presented 15J of absorbed energy at room temperature (21°C).
22
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - Testpiece aspectDf - Brittle Fracture

More from these cases

ML00183 — Ductile Behavior of an Aluminum WheelM - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Detail of the broken tensile specimen fracture surface. Predominantly dimples.
45
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Dimples
Tensile specimen fracture surface showing a small shrinkage and dimples, exactly as the WHEEL 1 fracture appearance (figure 7).
36
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Fracture
In the broken specimen fracture surface there are also regions of small cracks, that appear secondary, but that did not propagate. The predominantly mechanism is dimples.
38
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Cracks
Detail of the small cracks in a brittle phase, analyzed by EDS as rich in iron.
38
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Brittle Cracks
Ductile Behavior of an Aluminum Wheel
2
VIEW
ML00183 / Dec.2022
Ductile Behavior of an Aluminum Wheel
M - Aluminum Silicon MagnesiumP - CastingAp - AutomotiveCd - Ductile Behavior
Cm - Testpiece aspectDf - Fracture

+1 more from this case →

ML00173 — Welding Cracks in an Aged HP Cast FittingM - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Welding Cracks in an Aged HP Cast Fitting
3
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Testpiece aspectDf - Broken Testpiece