Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Capture method: Optical Microscope Detail focus: Intergranular Cracking clear all

UNS — sub-branches

A03560 1A96061 1C12000 1C28000 1C36000 1C60800 1C68700 1F32800 2G10050 1G10080 1G10200 2G10450 1G10550 1G10700 1G10800 1G12110 1G15220 mod 1G15240 1G41300 3G41400 2G43400 1G48200 1G61500 1J23055 1J91540 1K03101 2N02200 1N04400 1N07718 3N08705 1R50400 2R56400 1S15500 1S17400 3S17700 1S21800 2S30300 1S30400 4S30409 1S31600 4S31603 3S32304 1S32750 3S32760 2S42000 3S43100 mod 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect of the multiple intergranular cracks, initiating from the bottom of a pit.
25
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking
Micrography close to the external surface (to the top). The layer of intergranular corrosion shows evidences of selective leaching (suggesting that the aluminum was preferentially consumed). The stress corrosion cracking starts from the intergranularly corroded layer.
113
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Intergranular Cracking
Micrography of a longitudinal section of the bolt, in a position close to the fracture (top) and bolt surface (left ), presenting several secondary intergranular cracks.
57
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Intergranular Cracking
Micrography of a longitudinal section of the spring indicating that under the deposits there are intergranular cracks initiating at the spring surface.
72
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking
Micrography of the longitudinal section of the stud at the fracture (top of the figure) of a brittle intergranular aspect.
24
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a transverse section of the ring, showing the corroded martensitic structure (chemical dissolution) inside the pitting.
33
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking
Micrographic detail of the longitudinal section of the link, presenting internal cracks of intergranular morphology, typical of a hydrogen assisted mechanism.
52
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the connector, at the fracture surface (in the top), showing intergranular secondary cracks.
54
VIEW
ML00078 / Jun.2017
Hydrogen Cracking of IN 718 Subsea Connector
M - NiCrFe AlloyP - ForgingAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking

More from these cases

ML00172 — Brittle Fracture of a LAS Valve SpringM - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Micrographic detail of the intergranular cracks, initiating from the bottom of a pit.
29
VIEW
ML00172 / Mar.2021
Brittle Fracture of a LAS Valve Spring
M - Low Alloy Medium Carbon QTP - SpringAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Intergranular Cracking
ML00139 — Hydrogen Fracture of a 17-4 PH Allen BoltM - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the secondary intergranular cracks close to the surface of the bolt, where the fracture occurred.
56
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Intergranular Cracking
Micrographic detail of the intergranular cracks in the transition between the threaded body and the head of the non broken bolt, indicating that this bolt was also embrittled and could fail soon.
48
VIEW
ML00139 / Jun.2018
Hydrogen Fracture of a 17-4 PH Allen Bolt
M - Precipitation Hardened Stainless SteelP - Allen BoltAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
ML00137 — Brittle Fracture of a 15-5 PH Valve SpringM - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Micrographic detail of a longitudinal section of the spring indicating that under the deposits there are intergranular cracks initiating at the spring surface.
65
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - As polished micrographyDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the spring indicating that under the deposits there are intergranular cracks initiating at the spring surface.
60
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrography of a longitudinal section of the spring indicating that under the deposits there are intergranular cracks initiating at the spring surface.
57
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the spring indicating that under the deposits there are intergranular cracks initiating at the spring surface.
57
VIEW
ML00137 / Mar.2021
Brittle Fracture of a 15-5 PH Valve Spring
M - Precipitation Hardened Stainless SteelP - SpringAp - Oil and GasCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Micrographic detail of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface. it is possible to identify dissolution of the structure adjacent to the grain boundaries,
24
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrography of a transverse section, in the center of the ring, where the cracking was closed. The cracks are thin, not corroded, intergranular and not connected to the surface, indicating a hydrogen embrittlement effect.
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
ML00079 — Hydrogen Cracking of a Maritime Chain LinkM - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Micrographic detail of the longitudinal section of the link, close to the fracture surface, presenting the intergranular morphology of the secondary cracks, parallel to the fracture.
29
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of the intergranular secondary cracks, parallel to the fracture, typical of a hydrogen assisted cracking.
29
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking