Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Capture method: Longitudinal Section Aspect clear all

UNS — sub-branches

A03560 1A96061 1C12000 1C28000 1C36000 1C60800 1C68700 1F32800 2G10050 1G10080 1G10200 2G10450 1G10550 1G10700 1G10800 1G12110 1G15220 mod 1G15240 1G41300 3G41400 2G43400 1G48200 1G61500 1J23055 1J91540 1K03101 2N02200 1N04400 1N07718 3N08705 1R50400 2R56400 1S15500 1S17400 3S17700 1S21800 2S30300 1S30400 4S30409 1S31600 4S31603 3S32304 1S32750 3S32760 2S42000 3S43100 mod 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Macroscopic aspect after cutting longitudinally in two halfs, at the damaged area. The tube internal surface showed a red copper colour at the overheated region and the perforation is associated to longitudinal cracks.
104
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Longitudinal Section AspectDf - Internal Surface
Macrographic detail of the longitudinal section of the stub end, showing the external side to the top and the internal side to the bottom. There are multiple cracks starting from the external side.
54
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Longitudinal Section AspectDf - Multiple cracks
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
61
VIEW
ML00145 / Sep.2018
Impact of a .380 Winchester on 6061 T6 Plate
M - Aluminum Magnesium SiliconP - Rolled PlateAp - StructureCd - Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section
Longitudinal slice of the flanged sleeve, 180 mm long, in a macrography presenting the 1/2" tubular wall thickness where the sealing was applied. The external surface of the sleeve (seawater wet) is in the left side of the figure and the internal surface (oiled) is in the right side. The flange is to the top of the figure.
52
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Longitudinal Section AspectDf - General View
Aspect of a typical .308 Winchester projectile, similar to the one adopted to shot the plate, cut in a longitudinal section. It is a Cu alloy case filled with Pb-Sb.
34
VIEW
ML00144 / Aug.2018
Impact of a .380 Winchester on Ti64 Plate
M - Ti6Al4VP - Rolled PlateAp - StructureCd - Non-Pierced
Cm - Longitudinal Section AspectDf - Longitudinal Section
The longitudinal section of the pin shows that it was deformed in a localized position, where the layer was detached, top side of the figure. The pin wall was plastically deformed decreasing the internal diameter.
222
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - Longitudinal Section AspectDf - Plastic Deformation
Macrography of the longitudinal section of the broken link, at the fracture surface. There are several secondary cracks, parallel and perpendicular to the link axis.
37
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section
The longitudinal macrosection shows the fracture appearance, irregular, and a lot of secondary cracks transverse to the bolt axis, and longitudinal.
126
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Detail of the perforation point, internal view. Aligned perforations in the overheated region and interconnected longitudinal cracks.
94
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - Longitudinal Section AspectDf - Leakage
ML00146 — Plastic Deformation of a SDSS Riser PinM - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
The longitudinal section of the pin at the region of the thermal spray layer detachment, showing that the pin suffered a localized lateral bending with strong plastic deformation, responsible for the layer detachment. The figure shows the external surface (top of the figure) with the layer detachment (gray aspect), the thickness of the pin (deformed) and the internal surface (bright aspect).
124
VIEW
ML00146 / Jul.2018
Plastic Deformation of a SDSS Riser Pin
M - Super Duplex Stainless SteelP - PinAp - O&G Well DrillingCd - Bending
Cm - Longitudinal Section AspectDf - Plastic Deformation
ML00077 — Hydrogen Cracking of LAS Subsea BoltsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Several secondary cracks in the broken bolt, responsible for the irregular shape of the fracture, that presentes brittle cracks in the transverse and longitudinal directions.
109
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section