Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Electrolytic Etch Micrography by SEM clear all

UNS — sub-branches

A03560 2A08500 1A96061 1C12000 1C28000 1C36000 1C60800 1C68700 1C70600 1C85710 1C92200 1C95300 1F11701 1F32800 2F34800 1G10050 1G10080 1G10100 1G10200 2G10450 2G10500 1G10550 1G10600 1G10700 2G10800 2G10900 1G12110 1G15220 mod 1G15240 1G41300 4G41400 3G43400 1G48200 1G61500 1G86300 2J23055 1J91540 2J92900 1K03101 2K81340 1N02200 1N04400 1N07718 7N08705 1R50400 2R56400 3S15500 1S17400 3S17700 1S21800 2S30300 1S30400 4S30403 1S30409 1S31600 4S31603 3S32304 1S32750 5S32760 2S40900 2S41500 1S42000 3S43100 mod 1T31501 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail by scanning electron microscopy of the interface between the two thermal spray layers, the first one in stainless steel (bottom of the figure) and the second one, at the surface,in tungsten carbide (top of the figure). The composition of the first layer is similar to the base metal (lean duplex) and the composition of the second layer is WC in a Co matrix.
16
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Electrolytic Etch Micrography by SEMDf - Thermal Spray Layer
Image by scanning electron microscopy of the metallurgically bonded interface of the composite seamless tube (carbon steel externally claded with stainless steel), in the side of the stainless steel where a strain hardening effect plus a carbide precipitation in twins is shown. The hardness of this region (279 HV0.3) is a lot higher than the value obtained out of this region (167 HV0.3) for the same stainless steel.
814
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Clad Interface
Micrographic detail of the flange base metal presenting a coarse duplex ferritic austenitc structure and detrimental phases associated to the ferritic structure.
47
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Duplex structure
Micrographic detail of the cracking, associated to the ferrite network, that presents both corrosion (preferential dissolution) and fracture (clevage) aspects.
128
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Electrolytic Etch Micrography by SEMDf - Crack

More from these cases

ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Micrographic detail of the first thermal spray layer, in stainless steel with the same composition of the base metal (lean duplex).
16
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Electrolytic Etch Micrography by SEMDf - Thermal Spray Layer
Micrographic detail, by scanning electron microscopy, of the duplex, austenitic and ferritic, structure with sigma phase.
16
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - Electrolytic Etch Micrography by SEMDf - Sigma
ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
The scanning electron microscopy image details the strain hardened layer with carbide precipitation at twins, in the stainless steel side very close to the interface.
81
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Strain Hardened
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Micrographic detail of the flange base metal presenting a coarse duplex ferritic austenitc structure and detrimental phases associated to the ferritic structure.
39
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - Electrolytic Etch Micrography by SEMDf - Duplex structure
ML00002 — Preferential Dissolution and Cracks in SDSSM - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Micrographic detail of the ferrite network with evidences of precipitation/formation of detrimental phases. NaOH solution was adopted for the electrolytic etching.
86
VIEW
ML00002 / Jan.2018
Preferential Dissolution and Cracks in SDSS
M - Super Duplex Stainless SteelP - Fabrication WeldAp - PipingCd - Preferential Dissolution
Cm - Electrolytic Etch Micrography by SEMDf - Delta ferrite