UNS

3 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Vibration Induced Fatigue Microstructure: Austenite Capture method: Aspect Before Analysis clear all

UNS — sub-branches

N07718 1S30400 1S31600 1S31603 1

Results

SortNewestOldestTitle A-ZTitle Z-A
General view of the 2" branch line that was supporting an instrument in a 12" gas piping of an offshore unity. The branch line is composed by a seamless pipe welded to a weldolet (left side of the figure) and to a flange (right side of the figure). The leakage is associated to a through wall cracking in the middle of the pipe length. The cracking is not evidenced in the figure, since it is too thin. See the schematic drawing in the next figure
494
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - General View
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
498
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack

More from these cases

ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Aspect of the internal surface of the pipe after longitudinal cutting, presenting a straight cracking, circumferential. The weldolet is to the left side and the flange is to the right side. See the schematic drawing in the next figure.
89
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking
Aspect of the internal surface of the 2" nominal diameter pipe, SCH 40, presenting a circumferential through wall cracking in the pipe, not associated to any of the welded joints. It is possible to see the cracking parallel to the two welded joints: the pipe to weldolet (left side of the figure); and the pipe to flange (right side of the figure).
57
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Through Wall Cracking
Circumferential cracking in the middle of the pipe, view from the external side. Several pits close to the cracking.
57
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - External Surface
ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
xx
117
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - At the Surface
Macroscopic aspect of the 1" shaft fracture surface, revealing beach marks at the surface typical of fatigue, initiated from the surface of the spline shaft at the gear position.
121
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Fatigue Fracture