Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Zinc Layer Capture method: Aspect Before Analysis Detail focus: Brittle Fracture clear all

ASTM — sub-branches

Results

SortNewest Oldest Title A-Z Title Z-A

Aspect of the fracture surface of the 2" diameter casting. The fracture appeared flat, with secondary cracks, and the position of the fracture during the loading test is located in the region that was in tensile stress during the hot dip galvanized process (the part was sustaining its own weight during the zinc hot dip bath).

801

ML00138 / Jun.2018

Liquid Metal Embrittlement of a HSLA Steel

M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement

Cm - Aspect Before AnalysisDf - Brittle Fracture