ASTM

1 case · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Structure Microstructure: Tempered Martensite Capture method: Optical Microscope clear all

ASTM — sub-branches

A 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Tempered martensitic structure of the plate base metal.
93
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

More from these cases

ML00010 — Cold Cracks in a Gouged Weld MetalM - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Detail of the tempered martensitic structure of the plate base metal. Hardness level of 27 HRc.
92
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Low magnification micrography of a transverse section of the weld at the heat affected zone region. The macrosection was hardness tested and the base metal hardness is 27HRc, the HAZ is 32HRc and the weld metal is 45HRc, revealing something wrong in the weld metal at the position close to the cracked area.
79
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Transverse Section
High temperature heat affected zone of the plate, welded in repair. The micrography was taken from a sample collected close to the cracked region, but not containing any macroscopic cracking.
76
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Detail of the high temperature heat affected zone of the plate, welded in repair.
69
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
The weld metal, hard, presented a martensitic structure, probably due to the localized increase in carbon content, from the unsuitable carbon arc gouging procedure.
63
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal

+5 more from this case →