ASTM

4 cases · 47 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Chemical Industry Microstructure: Austenite clear all

ASTM — sub-branches

A 3B 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The scanning electron microscopy image of the internal surface of the tube in position 2 shows a localized corrosion region with intergranular morphology, as well a crack from the corroded region.
1237
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Surface Aspect by SEMDf - Intergranular Corrosion
Micrographic detail of the fatigue cracking at the margin of the flange to shell fillet weld.
485
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Fatigue Crack
Aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail. See the schematic drawing in the next figure
371
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Aspect by NDTDf - Through Wall Cracking
Transverse section of the fitting that suffered a longitudinal cracking. As polished. The wrought fitting has suffered intergranular stress corrosion cracking from the internal surface, exposed to hot caustic environment.
566
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Micrography by OMDf - Intergranular Cracking

More from these cases

ML00086 — Intergranular Corrosion of Sensitized 304SSM - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in the colder part of the equipment, position 1. The material presented carbide precipitation at grain boundaries (not yet fully surrounding the grains) and at this point the tube presented no internal corrosion.
338
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 2, where the temperature was higher and the carbide precipitation increased during service.
272
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Precipitation
Micrography of the 1.65 mm thickness tube, in the middle of the thickness of the longitudinal section. This part of the tube is located in position 3, where intergranular and transgranular carbide precipitation occurred during service.
234
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intragranular Secondary Precipitation
The low magnification image of the internal surface of the tube, in position 2, shows several points of localized corrosion, with intergranular morphology.
193
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Surface Aspect by SEMDf - Intergranular Corrosion
Micrography of a longitudinal section of the tube in position 2, presenting thinning by intergranular corrosion at the internal surface.
193
VIEW
ML00086 / Nov.2017
Intergranular Corrosion of Sensitized 304SS
M - Austenitic Stainless SteelP - Seamless tubeAp - Heat ExchangerCd - Intergranular Corrosion
Cm - Micrography by OM using A262 Method ADf - Intergranular Corrosion

+3 more from this case →

ML00050 — Fatigue Failure of a 316SS Pressure StabilizerM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Aspect of the equipment presenting a through wall cracking at the margin of the fillet weld.
143
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Macrography of the welded joint between the flange and the shell, indicating the position where the cracking was detected, at 90°.
117
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Welded Joint
The shell plate micrography showed an austenitic structure.
101
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
The macrography of a transverse section of the shell to flange weld (Lepto's etch) shows that the cracking occurred through the shell plate thickness, at the margin of the fillet weld.
93
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Transverse Section AspectDf - Cracking
Fracture surface after opening the shell cracking, presenting fatigue striation. The fracture presents also foreign particles.
132
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+3 more from this case →

ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Schematic drawing presenting the aspect of the cracking after Dye Check Test (Liquid Penetrant) in the external side of the line that operates at 800°C, insulated, and presented the leakage associated to the longitudinal seam weld of the fitting. The circumferential butt weld of the fitting to a pipe did not fail.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Identification drawingDf - Through Wall Cracking
Aspect of the internal side of the fitting, at the longitudinal seam weld, and macrography of a transverse section showing the through wall cracks.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Transverse Section
Through wall cracking in the longitudinal seam weld of the fitting. Several cracks, longitudinal to the weld, were created by the connection of voids in the weld metal, associated to a strong microstructural evolution.
191
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Cracks
Micrography of a longitudinal section of the fitting, at the base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
44
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrographic detail of the fitting base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal

+10 more from this case →

ML00011 — Intergranular SCC of Pure NickelM - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
The fitting presented through wall cracks that lead to leaking. The internal aspect of the surface is presented where the cracks were still in the begining.
127
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Crack
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
114
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
110
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
Microstructure of the fitting in the transverse section, presenting a granular Ni austenitic structure. No evidences of any phase in the grain boundaries.
96
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Kalling Etched Micrography by OMDf - Austenite
After opening the crack the fracture surface presented different aspects close to the internal surface and through the wall propagation. Intergranular at the surface, showing intergranular SCC mechanism, and transgranular with striation, showing the contribution of pulsing loads.
101
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Fractography by SEMDf - Through Wall Cracking

+7 more from this case →