Crevice Corrosion in a Subsea System — Aspect Before Analysis

ASME — sub-branches

B18.3 1B36.19 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractographic analysis by scanning electron microscopy of the stud fracture surface after opening the cracks. Brittle intergranular morphology with dimples and quasecleavage micromechanisms indicate that the internal cracks, intergranular, occurred by a hydrogen embrittlement effect during electroplating, and the ductile aspects are probably associated to overloading during torque.
517
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Fracture
The main pipe, ND 18", has suffered a pipe through wall cracking at the margin of the 1 1/2" branch socket weld.
664
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Crack

More from these cases

ML00127 — Hydrogen Cracks of Cadmium Plated StudsM - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Allen stud, 1/2" nominal diameter, cadmium plated and chromate treated, cracked during assembling external parts in a gate valve.
63
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Macrography of a longitudinal section of the stud, showing the flat fracture of brittle aspect.
46
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - NItal Etched MacroDf - Longitudinal Section
Allen stud, 1/2" nominal diameter, cadmium plated and chromate treated, cracked during assembling external parts in a gate valve.
40
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture
Allen stud, cadmium plated and chromate treated. The fracture appearance is brittle.
38
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture
Fractographic analysis by scanning electron microscopy of the stud fracture surface after opening the cracks. Brittle intergranular morphology with dimples and quasecleavage micromechanisms indicate that the internal cracks, intergranuar, occurred by a hydrogen embrittlement effect during electroplating, and the ductile aspects are probably associated to overloading during torque.
37
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking

+10 more from this case →

ML00006 — Vibration Induced Fatigue in 304SSM - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
The macro section transverse to the welded region, show that the through wall cracking occurred in the pipe base metal, from the margin of the weld.
191
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Through Wall Cracking
Macro transverse to the weld showing that the fracture occurred in the main pipe, at the margin of the weld.
163
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Fracture
The fracture surface of the main pipe is presented in low magnification (external pipe surface in the top) showing a flat propagation starting from the contour of the weld margin.
173
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Margin of the Weld Crack
Fracture surface micromechanism by striation, evidence of FATIGUE.
158
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation
Fracture surface micromechanism by striation, evidence of FATIGUE.
147
VIEW
ML00006 / Apr.2017
Vibration Induced Fatigue in 304SS
M - Austenitic Stainless SteelP - Longitudinal Seam Welded PipeAp - PipingCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Striation

+4 more from this case →