Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Bainite Capture method: NItal Etched Macro clear all

API — sub-branches

5CT 15L 3

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography showing the different regions of a pipe-to-plate fillet weld. See the schematic drawing in the next image
954
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Fracture
The macrography of a longitudinal section of the pipe and connector, at the welded joint, shows that the welding was conducted from both side of the groove, starting from the ID and finishing from the OD, ID later machined flush. The cracking was detected by ultrasonic test and the macro shows that it is at the fusion line, growthing into the weld metal. See the schematic drawing in the next figure
535
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Longitudinal Section

More from these cases

ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Macrography of the fillet welded joint between the 3" ND tube and the 3/4" thick plate. See the schematic drawing in the next figure
56
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint
ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Hot cracking at the fusion line of the connector side, in a welded joint between a forging and a pipe, in a macrographic sample. The region of the heat affected zone of the connector presents a dendritic aspect suggesting that the forging reduction rate of the connector was not too high and did not broke the cast structure.
110
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint