Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Surface Aspect clear all

AISI — sub-branches

1010 11020 11045 11070 1304 1304L 1310 1316 5347 Nb stabilized 1409 1410 24130 54140 4420 24330V 14340 24820 16150 28620 18630 1D2 1Dual grade 316/316L 1

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification microscope image showing the aspect of the thread close to the fracture surface. Looks like a wear or strong corrosion, but in fact the threads were removed because they were cracked, as can be seen in the next figures.
67
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Surface AspectDf - Low Mag
Aspect of the cut surface of the fork tooth in the scoop. The thickness is 1 mm and the fabrication finishing of the surface is polished. The tooth in the center was cut for analysis in the longitudinal section.
33
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Surface AspectDf - Cut Surface
Detailed aspect of the cracks in the internal diameter surface, where the hardness level was too low. These are typical overloading cracks.
76
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Surface AspectDf - Cracks
The macroscopic aspect of the surface after preparation. Grinding and polishing.
50
VIEW
ML00092 / Sep.2017
MIC of a Valve Body
M - Martensitic Stainless SteelP - Valve BodyAp - Oil and GasCd - Brittle Behavior
Cm - Surface AspectDf - Localized Corrosion
Detail of the rusted surface of the knife, before cleaning.
340
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Surface AspectDf - Corrosion