Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: High Temperature Capture method: Naked Eye or Stereoscope clear all

A — sub-branches

193 1213 1297 2403 1532 1

Results

SortNewestOldestTitle A-ZTitle Z-A
The macrography of a longitudinal section shows that the tube did not present local thinning in any region, but the internal and external scales are evidenced. The external surface (OD) is to the top of the figure and the internal surface (ID) is to the bottom of the figure.
124
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - NItal Etched MacroDf - Longitudinal Section
The macrography of a transverse section of the new tube shows that there are shrinkage voids close to the internal surface, that is exposed to high temperature air. The tube is a 4" diameter and 1/4" thick.
62
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure
Aspect of the internal side of the fitting, at the longitudinal seam weld, and macrography of a transverse section showing the through wall cracks.
62
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Transverse Section
Macrography of the NEW TUBE, centrifugally cast, in the transverse section, presenting columnar grains close to the external surface.
50
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section

More from these cases

ML00097 — Cast SS Tube Removed From High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
The macrography of a transverse section of the tube removed from service after 6 months, with damage close to the internal tube surface. The tube is a 4" diameter and 1/4" thick.
41
VIEW
ML00097 / Nov.2017
Cast SS Tube Removed From High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - High Temperature
Cm - Transverse Section AspectDf - Casting Structure
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Macrography of the TUBE REMOVED FROM SERVICE, centrifugally cast, in the transverse section, presenting thickness loss and macrostructure deterioration.
33
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Kalling Etched MacroDf - Transverse Section