Rectangular Tube

1 case · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Optical Microscope Detail focus: Sampling and Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
SAMPLE 1 AT THE FRACTURE - Micrography in low magnification where the thickness is reduced to zero (fracture). Side A (process side) to the bottom and side B (furnace environment side) to the top.
85
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag

More from these cases

ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
SAMPLE 1 AT 1 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation.
77
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
SAMPLE 2 AT 2 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation. No variation in the microstructure of the center of the plate, compared to sample 1.
52
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Low Mag
SAMPLE 3 AT 4 mm THICKNESS - Micrography in low magnification in the center of the thickness. The microstructure is austenitic with secondary intergranular and intragranular precipitation, but this micrography was obtained in the longitudinal section, presenting the plate alignment and was etched with NaOH, adopted to colour the sigma phase .
40
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - NaOH Electrolytic Etched MicroDf - Low Mag
SAMPLE 1 AT 1 mm THICKNESS - Micrography in low magnification in the center of the thickness, as polished. There are no regions of internal damage (like internal voids or cracks), indicating that the mechanism is only related to surface effects.
42
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - In the Center of the Thickness
SAMPLE 3, CLOSE TO THE SURFACE OF SIDE A - Micrography, as polished, of the oxides at the process side. In this region there is an oxide layer, not continuous but with no localized penetrations.
43
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface

+3 more from this case →