Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Welding Defect Detail focus: Weld Metal clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The weld metal presented a ferritic/bainitic structure at the surface, where the replica was conducted. The weld metal hardness is 272 HB, too high for this material, suggesting lack of a suitable PWHT.
102
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital etched, OMDf - Weld Metal

More from these cases

ML00071 — Reheating Cracking of a CrMo Vessel WeldM - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
A small sample containing cracks was removed from the cracked weld metal, by mechanical means.
81
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Transverse Section AspectDf - Weld Metal
Macrographic aspect of a transverse section of the sample with multiple cracks that were deep in the weld metal.
71
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - NItal Etched MacroDf - Weld Metal