Forging

1 case · 1 image

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Segregation Bands Detail focus: Welded Joint clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Hot cracking at the fusion line of the connector side, in a welded joint between a forging and a pipe, in a macrographic sample. The region of the heat affected zone of the connector presents a dendritic aspect suggesting that the forging reduction rate of the connector was not too high and did not broke the cast structure.
110
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - NItal Etched MacroDf - Welded Joint