Rectangular Tube

1 case · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: At the Surface clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
SAMPLE 3, CLOSE TO THE SURFACE OF SIDE A - Micrography, as polished, of the oxides at the process side. In this region there is an oxide layer, not continuous but with no localized penetrations.
43
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface

More from these cases

ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
SAMPLE 3, CLOSE TO THE SURFACE OF SIDE B - Micrography, as polished, of the oxides at the electric furnace environment side. In this region the oxide layer is thinner than in the process side.
46
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface
SAMPLE 1, CLOSE TO THE SURFACE OF SIDE A - Micrography, as polished, of the oxides at the process side. In this region the oxide layer is penetrating into the austenitic grain boundaries, creating a crack like effect.
56
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - At the Surface
SAMPLE 1 AT 1 mm THICKNESS, SIDE B - Micrographic detail of the austenite with secondary precipitation, close to the surface exposed to the furnace environment. This NaOH electrolytic etch is adopted to colour sigma phase and at this position there are no special formation of sigma in the grain boundaries and there are no oxide penetrations, confirming that the environment is important to create the damage and the internal side of the tube is responsible for the quick degradation in high temperature.
25
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - NaOH Electrolytic Etched MicroDf - At the Surface