Coated Product

1 case · 15 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: G41300 clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the fracture surface of the bolt, after cleaning with a plastic brush. Although there is a layer of oxides it is possible to see the intergranular morphology of the fracture, typical of a hydrogen embrittlement mechanism.
1154
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture

More from these cases

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Detailed aspect of the fracture surface of the bolt, evidencing the intergranular morphology of the fracture (although with an oxide scale), typical of a hydrogen embrittlement mechanism.
114
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture
Aspect of the broken bolt, 5/8" Allen, socket head cap screw, originally 1 3/4" long, broken in subsea service under cathodic protection. The bolt presents a zinc coating.
116
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Micrography of the longitudinal section of the bolt showing a martensitic structure, with segregation bands evidenced by the chemical etch.
99
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Banded Structure
Micrography of the longitudinal section of the bolt at the bottom of the thread fillet, showing the uniform martensitic structure, not strain hardened.
90
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Uniform Structure
Micrography of the longitudinal section of the bolt at the top of the thread fillet, showing a small circunferential cracking typically of a rolling process to manufacture the thread. The thread presented no evidences of plastic deformation suggesting that the heat treatment was applied later. It is important to mention that this cracking presented no influence in the fracture of the bolt.
101
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Rolled Thread

+9 more from this case →