Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
In a cut perpendicular to the macroscopic secondary crack it is possible to see several brittle microcracks (branched), indicating that an embrittlement has occurred.
22
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - As polished micrographyDf - Brittle Cracks
Original casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
50
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Left Side
Transverse section of the blade showing large grains of this poliycristaline cast material.
421
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coarse Structure

More from these cases

ML00176 — Hydride Formation in a Titanium BladeM - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
The main crack is to the top and the blade surface is to the right, in this micrography that does not reveal any plastic deformation, with transgranular and integranular cracks.
24
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Brittle Fracture
Transgranular and integranular cracks in the alpha matrix full of acicular hydrides .
17
VIEW
ML00176 / Nov.2021
Hydride Formation in a Titanium Blade
M - Unalloyed TitaniumP - BladeAp - Oil and GasCd - Hydride Formation
Cm - Micrography by OM, HF + HNO3 + H2O etchDf - Hydride Formation
ML00055 — CA6NM Blade Remanufactured by WeldingM - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Inserted casting base metal presenting a coarse martensitic structure with a small amount of delta ferrite.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - Base Metal Right Side
Micrography of the original casting blade at the fusion line of the welding with the insert casting. There is a refinement effect on the coarse base metal structure.
24
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Left Side
Micrographic detail of the fusion line of the original casting blade welded to the insert casting. There is a refinement effect on the coarse base metal structure.
21
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Left Side
Micrography of the inserted casting at the heat affected zone of the welding with the original casting. There is a refinement effect on the coarse base metal structure.
20
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Right Side
Micrographic detail of the fusion line of the inserted casting welded to the original casting. There is a refinement effect on the coarse base metal structure.
15
VIEW
ML00055 / Apr.2017
CA6NM Blade Remanufactured by Welding
M - Martensitic Stainless SteelP - Remanufacture by WeldingAp - EnergyCd - Removed From Service
Cm - Kalling Etched Micrography by OMDf - HAZ Right Side

+2 more from this case →

ML00042 — Gas Turbine Blade IN 939, CoatedM - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Micrography close to the surface of the blade, showing the diffusion coating (aluminum base alloy) that is still sound. No strong oxidation or erosion was detected.
53
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coating
Micrography as polished of the region where there was a refrigeration hole, presenting a cracking.
35
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by OMDf - Cracking
The cracking from the refrigeration hole presents an intergranular morphology, as shown in the micrography of a transverse section of the blade.
35
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Intergranular Cracking