Condition of the joint between the centrifugally cast tube (bottom) and the buttered fitting (top). During this welding the cast fitting (buttered) showed several cracks but after removal of the fitting it was clear that the cracks were formed during the buttering and not during the joining.
47
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Aspect Before AnalysisDf - General View
Aspect as received, side A, of the part removed from the rectangular tube that was manufactured from plates, and originally presented two welded seams (not included in the sample). Close to the edges of the sample, where probably were the corners of the rectangular tube, the degradation is in a highest level. Three samples were analysed, with different thicknesses (indicated in the figure). Side A is the side that was in contact with the reaction (product side).
445
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Aspect as received, side B, of the same part. Side B is the external side of the rectangular tube, that was in contact with the electric furnace atmosphere. This surface of side B presented less degradation than the internal surface (side A).
88
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Aspect Before AnalysisDf - General View
High Temperature Degradation of 310SS
2
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Aspect Before AnalysisDf - General View