Large Grains

2 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Microstructure clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Tempered martensitic structure for the F22 forging base metal.
129
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
Transverse section of the blade showing large grains of this poliycristaline cast material.
421
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coarse Structure

More from these cases

ML00178 — Cold cracks in Cr-Mo Welded ForgingM - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Grain coarsened martensitic heat affected zone. The hardness values about 270HV10 indicates that the joint was post welding heat treated (PWHT).
97
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Fusion line at the forging side. The weld metal to the top and the heat affected zone to the bottom.
84
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Fusion Line
Detail of the quenched and tempered martensitic structure at the heat affected zone.
64
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
Tempered martensitic structure at the weld metal in the cap.
56
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
ML00042 — Gas Turbine Blade IN 939, CoatedM - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Micrography of the blade, view inside the grain. The intragranular precipitation presents one unique size of precipitation, not yet coalesced, although the blade was in high temperature service for 50.000 hours. Etched by H2SO4 + HNO3 + H3PO4 reagent.
66
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Intragranular Secondary Precipitation