Granular

3 cases · 10 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Standard: B Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
SEM fractograph at 1200x magnification showing an intergranular fracture surface with angular, faceted grains and fine feather-like markings.
86
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
Aspect of the internal surface of the pipe at the welded region, showing the interface of the thinning area in the weld and the pipe base metal.
128
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Surface Aspect by SEMDf - Localized Thinning
After opening the crack the fracture surface presented different aspects close to the internal surface and through the wall propagation. Intergranular at the surface, showing intergranular SCC mechanism, and transgranular with striation, showing the contribution of pulsing loads.
101
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Fractography by SEMDf - Through Wall Cracking

More from these cases

ML00041 — Fatigue Fracture of Inconel 718 Spline ShaftM - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Microscopic detail of the transgranular striation in the fracture surface.
78
VIEW
ML00041 / Jun.2017
Fatigue Fracture of Inconel 718 Spline Shaft
M - NiCrFe AlloyP - ShaftAp - Oil and GasCd - Vibration Induced Fatigue
Cm - Fractography by SEMDf - Fatigue Fracture
ML00005 — Environmental Hydrogen Damage in Ti PipeM - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Region of the localized thinning at the weld metal, in a metallographic section, as polished. In the base metal the hydride layer is continuous and no thinning is evident (left side of the figure) and in the weld metal it is detached and cracked (right side of the figure).
107
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by SEMDf - Localized Thinning
Hydride layer at the internal surface of the pipe base metal, after Kroll etch.
71
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by SEMDf - Hydride Formation
Detail of the hydride layer at the internal surface of the pipe base metal, after Kroll etch.
62
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by SEMDf - Hydride Formation
ML00011 — Intergranular SCC of Pure NickelM - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
After opening the crack the fracture surface presented different aspects close to the surface, initiation mechanism, and through the wall propagation. Detail of the intergranular cracking mechanism close to the internal surface.
98
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Fractography by SEMDf - Intergranular Cracking
After opening the crack the fracture surface presented different aspects close to the internal surface, in the initiation, and through the wall propagation. Detail of the transgranular striation, showing the contribution of pulsing loads.
98
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Fractography by SEMDf - Fatigue Striation
After opening the crack the fracture surface presented different aspects close to the internal surface, in the initiation, and through the wall propagation. Detail of the transgranular striation, showing the contribution of pulsing loads.
82
VIEW
ML00011 / Oct.2017
Intergranular SCC of Pure Nickel
M - Unalloyed NickelP - Wrought FittingAp - Chemical IndustryCd - Stress Corrosion
Cm - Fractography by SEMDf - Fatigue Striation