Ferritic

2 cases · 21 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: AISI Detail focus: Sampling and Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Decorative table service fork, with a non metallic handle that is broken. The metallic part is about 165 mm long and presents two shapes: the scoop and the handle. The scoop is 53mm wide and 73mm long and the handle is about 9 mm wide and 75 mm long.
731
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite structure in the columnar (previous austenitic) grains has suffered degradation due to the long heat treatment cycle (12 hours) in high temperature.
97
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal

More from these cases

ML00151 — Ferritic Stainless Steel of a Flatware ForkM - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Micrography of the fork handle in the transverse section, curved, presenting differences between grain size and morphology. In the middle section there are elongated grains and close to the surfaces there are smaller and more equiaxed grains.
82
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Transverse Section
Lateral view of the fork showing the profile. The scoop convex depth is 10 mm and the handle concave depth is 3 mm. The overal thickness of the part is 1 mm.
53
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Aspect Before AnalysisDf - General View
Micrography of a longitudinal section of the fork, at the scoop to handle position (scoop to the right of the figure and handle to the left). The full thickness is presented in the image and it is possible to see that in the handle location the ferritic grains are larger in the center of the thickness than close to the surfaces, and in the scoop position the grains tend to be more uniform through the thickness.
50
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Longitudinal Section
Micrography of a fork longitudinal section, at the handle (close to the transition betwee the scoop and handle). The full thickness is presented in the image and it is possible to see that the ferritic grains are larger in the center of the thickness than close to the surfaces.
49
VIEW
ML00151 / Dec.2018
Ferritic Stainless Steel of a Flatware Fork
M - Ferritic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Typical manufacturing
Cm - Micro by OM, HCl + Ethanol + Picric AcidDf - Longitudinal Section
ML00129 — Non qualified WPS for High Strength SteelM - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Micrography of the weld metal, at the face, presenting regions of large ferritic grains. The acicular ferrite has suffered degradation due to the long heat treatment cycle (12 hours) in a temperature of 640°C, that is higher than the recommended for the D2 filler metal.
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Nital Etched Micrography by OMDf - Weld Metal
Macrography of the welded joint taken from the vertical up part of the joint, presenting the root in one pass, the fill of the joint in three passes, the cap in three passes and two temper bead passes. The 10" diameter tube, 9.5mm thick, was welded by GTAW in the root (80SD2 filler metal) and by SMAW for fill, cap and temper bead passes (10018-D2 filler metal).
78
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - NItal Etched MacroDf - Welded Joint
WPS welded in 6G qualification welding position and tested according to ASME IX and NACE ISO 15156. Minimum preheating of 250°C. Two temper bead passes. PWHT at 640°C during 12 hours. Tube diameter 10". Thickness 3/8". V groove 70°. Root opening 1/8". NOT APPROVED due to ULTIMATE STRENGHT lower than the base metal minimum requirements.
87
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - WPS summaryDf - Welded Joint
Aspect of the internal surface of the tube, presenting the aspect of the root, after welding and heat treatment.
63
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Aspect Before AnalysisDf - Internal Surface
Aspect of the external surface of the tube, presenting the aspect of the cap and temper bead passes, after welding and heat treatment.
54
VIEW
ML00129 / Apr.2018
Non qualified WPS for High Strength Steel
M - Low Alloy Medium Carbon QTP - Welded Testpiece for QualificationAp - Oil and GasCd - Non qualified
Cm - Aspect Before AnalysisDf - External Surface

+10 more from this case →