Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: API Capture method: Aspect Before Analysis Detail focus: Sampling and Analysis clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the 4" pipe that was in seawater service for 8 years and leaked in a longitudinal line that corresponds to the seam weld. The internal surface presented thick deposits. Although the pipe was cut with a thermal process, the analysis was conducted after mechanical cutting.
100
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - General View
The connector was welded to the pipe from both (internal and external) sides, a PWHT was applied and the part was machined. The UT indication was detected during final inspection.
78
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00140 — Preferential Corrosion of Pipe Seam WeldM - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Aspect of the internal surface of the pipe after cleaning, showing the leakage line.
67
VIEW
ML00140 / May.2019
Preferential Corrosion of Pipe Seam Weld
M - Low Carbon SteelP - Longitudinal Seam Welded PipeAp - ShipCd - Preferential Dissolution
Cm - Aspect Before AnalysisDf - Internal Surface