Coating Layer

3 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: UNS Capture method: Scanning Electron Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the coaster surface grooves, by scanning electron microscopy in a low magnification, showing in the right side the flat region that serves as a support; and in the left side the decorative grooves. The smooth surface in the groove suggests that the coasters were manufactured by casting.
66
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Fractographic analysis by scanning electron microscopy of the stud fracture surface after opening the cracks. Brittle intergranular morphology with dimples and quasecleavage micromechanisms indicate that the internal cracks, intergranular, occurred by a hydrogen embrittlement effect during electroplating, and the ductile aspects are probably associated to overloading during torque.
517
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Fracture
Aspect of the fracture surface of the bolt, after cleaning with a plastic brush. Although there is a layer of oxides it is possible to see the intergranular morphology of the fracture, typical of a hydrogen embrittlement mechanism.
1154
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture

More from these cases

ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Detail of the previous photo showing the flat surface in the right side and the grooves in the left side. The flat side is scratched and the grooves presented a smooth finishing (with dendritic morphology).
57
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Detail of the flat scratched region of the coaster surface. The dark grey "nodules" are lead (Pb) base inclusions.
50
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
Detail of the groove region, showing a typical casting morphology at the surface: smooth and presenting a dendritic aspect with interdendritic shrinkage. Some dark grey "nodules" with Pb inclusions are also observed.
51
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - At the Surface
There are some regions in the coaster surface where pores associated to shrinkage is evident.
49
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - Surface Aspect by SEMDf - Casting defects
ML00127 — Hydrogen Cracks of Cadmium Plated StudsM - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Fractographic analysis by scanning electron microscopy of the stud fracture surface after opening the cracks. Brittle intergranular morphology with dimples and quasecleavage micromechanisms indicate that the internal cracks, intergranuar, occurred by a hydrogen embrittlement effect during electroplating, and the ductile aspects are probably associated to overloading during torque.
37
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Cracking
ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Detailed aspect of the fracture surface of the bolt, evidencing the intergranular morphology of the fracture (although with an oxide scale), typical of a hydrogen embrittlement mechanism.
114
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Intergranular Fracture