Coating Layer

1 case · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Condition: Localized Dissolution Capture method: Optical Microscope clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
As polished micrographic aspect of the longitudinal section of the cylinder, at the surface, in a region where the damage is in the begining. It is possible to see that there are two layers at the surface. A first Ni layer, 300HV average hardness, over the low carbon steel substrate, 200HV average hardness, and a chromium plated layer, 1100HV average hardness and several discontinuities.
62
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Micrography by OMDf - Longitudinal Section

More from these cases

ML00128 — MIC of a Stored Hydraulic CylinderM - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Micrographic aspect of the Cr layer at the surface presenting incipient damage. Microcracks of the Cr layer, associated to small pits.
62
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Micrography by OMDf - Cracks
Micrographic aspect, after Nital etching, of the longitudinal section of the cylinder, at the surface, in a region where the damage is in the begining. There are two layers at the surface. A first Ni layer, 160 microns thick and 300HV average hardness, over the low carbon steel substrate, 200HV average hardness, and a chromium plated layer, 250 microns thick and 1100HV average hardness.
59
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corrosion
Micrographic detail of the longitudinal section of the cylinder, at the surface, in a region where the Cr layer is detaching.
56
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corrosion
Micrographic aspect of the longitudinal section of the cylinder steel substrate, presenting a ferritic-pearlitic structure.
207
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrographic detail of the ferritic-pearlitic structure of the cylinder steel substrate.
41
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite

+3 more from this case →