Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Removed From Service clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a ring transverse section presenting a large variation in the grain size, revealing the diferences in the solidification rate.
453
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O solution Etched MacroDf - Casting Structure
The micrography of the transverse section shows coarse grains and biphasic structure. Alpha grains and a lamellar eutectoid structure can be observed in the material.
464
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface

More from these cases

ML00166 — Tin Bronze Wear Ring of Seawater PumpM - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Low magnification micrography of a transverse section of the ring showing a dendritic structure.
64
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of a transverse section of the ring showing a cored alpha structure with segregation at interdendritic regions. This structure is in a region close to the ring surface.
52
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of a transverse section of the ring showing a cored alpha structure with strong segregation at interdendritic regions, and regions of a white structure at grain boundaries. This structure is in a region close to the center of the ring.
51
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrographic detail of the cored alpha structure with light segregation at intergranular regions (light layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the ring surface, where the solidification was quicker.
49
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
Micrographic detail of the cored alpha structure with strong segregation at intergranular regions (dark layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the center of the ring, where the solidification was slower.
47
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics

+2 more from this case →

ML00044 — Centrifugally Cast CuAl BushingM - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Micrographic detail of the structure at the external surface.
58
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the External Surface
The micrography of the transverse section shows coarse grains and biphasic structure. No diferentes close to the internal surface. Alpha grains and a lamellar eutectoid structure can be observed in the material.
46
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Micrographic detail of the structure at the internal surface.
38
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - Close to the Internal Surface
Detail of the structure in the center of the thickness. Alpha grains and lamellar eutectoid structure.
28
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - NH4OH+H2O+H2O2 Etched MicroDf - In the Center of the Thickness
The macrography of the transverse section shows the columnar grains typical of a centrifugally cast material. The etch is the same as the adopted for the micrographies. The bushing thickness is 1/2".
41
VIEW
ML00044 / Feb.2017
Centrifugally Cast CuAl Bushing
M - Aluminum BronzeP - Cast BushingAp - EngineCd - Removed From Service
Cm - Transverse Section AspectDf - Columnar Grains