Alpha & Beta

2 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Capture method: As polished micrography clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Metallographic aspect of the polished surface of the (back of the) coaster, showing pores and shrinkages, typical of a casting structure.
49
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polished micrographyDf - Casting Structure
Micrography of the transverse section of the platesheet at the interface between the corroded and the non-corroded regions. The micrography is in the as polished condition.
140
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Preferential Dissolution

More from these cases

ML00156 — Antique Silver Plated Decorative PieceM - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Same region of the previous image but is a higher magnification, showing the metallographic aspect of the polished surface of the (back of the) coaster. Shrinkage with a dendritic morphology typical of a casting structure.
48
VIEW
ML00156 / Jan.2020
Antique Silver Plated Decorative Piece
M - BrassP - Decorative PieceAp - OrnamentalCd - Non Destructive Examination
Cm - As polished micrographyDf - Voids
ML00125 — Dezincification of a Cooler TubesheetM - BrassP - PlateAp - ShipCd - Preferential Dissolution
Micrography of the transverse section of the platesheet showing that part of the material (right side in the top of the figure) was lost (corroded).
129
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Preferential Dissolution
Micrographic detail of the dezincification effect, where the beta phase is preferentially corroded, leaving a cooper rich phase (red) that is porous and easily cracks.
121
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Dezincification
Micrographic detail of the dezincification effect, where the beta phase is preferentially corroded, leaving a cooper rich phase (red) that is porous and easily cracks.
130
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Cracks
Micrography showing detachment of material at the surface of the platesheet. The cracks are associated to the dezincification effect, where the beta phase was preferentially corroded and became a weak porous layer.
113
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Crack
Micrography presenting the interface between the layer where the dezincification occurred (top of the figure) and the region where the material was not yet corroded (bottom of the figure).
86
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Dezincification